Fatigue of vanadium-hydrogen alloys
Loading...
Authors
Lee, Kyung Sub
Issue Date
1976-12
Type
Electronic thesis
Thesis
Thesis
Language
ENG
Keywords
Materials engineering
Alternative Title
Abstract
S-N data obtained from stress-controlled fatigue tests revealed a pronounced improvement in fatigue life for hydrided vanadium, but little or no effect for 132 ppm hydrogen in solution. Similarly, strain-control tests showed no effects of hydrogen in solution on either cyclic hardening for fatigue life, in marked contrast to decrease in low cycle life for vanadium containing hydride plates.
Description
December 1976
School of Materials Engineering
School of Materials Engineering
Full Citation
Publisher
Rensselaer Polytechnic Institute, Troy, NY